Krivoy Rog mica tape, micanite sheet, basalt slab, BTSh cord, covelite slab, ShPGT-450 slab

Krivoy Rog mica tape, micanite sheet, basalt slab, BTSh cord, covelite slab, ShPGT-450 slab

Tape LSEP-934 TPL is a three-layer composition of fiberglass, mica paper and polyethylene terephthalate film impregnated with an epoxy-polyester binder.
Tape LSEP-934 TPL is used for case and coil insulation of traction electrical machines and large high-voltage electrical machines with voltage up to 6 kV with insulation systems of heat resistance class F. The tape is flexible in room environment. Suitable for manual and mechanized winding.
LSEP 934 tapes replace mica tapes of heat resistance classes B and F. Curing time: 10 - 16 hours at 160°C.
After baking several layers of mica tape, a homogeneous monolithic insulation is obtained. When the already cured mica tape is heated to a temperature of 100-120°C, the insulation becomes flexible, which allows the sections to be laid in the groove without damage to the insulation.
In the manufacture of tapes, paper produced from natural phlogopite mica is used without destroying its crystalline structure, which ensures increased dielectric properties of the tapes.
Tape designations:
LS - mica tape;
EP-934 grade of epoxy-polyester binder, heat resistance class F.
Tape LSK-T is a composition consisting of mica paper and one layer of electrically insulating fiberglass impregnated and glued together with an organosilicon binder.
BASIC PROPERTIES:
The LSK-T tape is distinguished by the simultaneous use of both mica and silicone as a heat-resistant barrier in its construction. Under the influence of high temperatures, silicone forms a polymer of siloxane units, which firmly holds the entire tape composition from destruction.
APPLICATION AREA:
Tape LSK-T is designed to create a dielectric barrier between the individual conductors of fireproof cable products of the ng(A)-FRLS and ng(A)-FRHF versions and must ensure continuous operation of the fire-resistant cable under a working load in fire conditions or high temperatures up to 900 ° C . In addition, it is possible to use LSK-T tape as an electrical insulating material of heat resistance class
"C" (220 °C) for the production and repair of electrical machines, incl. in technologies for creating an insulation system for electrical machines operating in the nuclear industry.
Tape LSK-T should be produced in rollers without breaks with a diameter of 220-320 mm and a width of 4; 5; 6; 8; 10; 15; 20; 25;
thirty; 35; 40; 45; 50 mm, tightly wound on a rigid sleeve with an internal diameter of 76 ± 1 mm.
The packaging must comply with the requirements of TU 3492-050-31885305-2013, the marking must comply with the requirements of GOST 26103-84 and TU 3492-050-31885305-2013.
Guaranteed shelf life of LSK-T brand tape (subject to storage and transportation conditions in accordance with GOST 26103-84 and TU 3492-050-31885305-2013) is 12 months from the date of manufacture.
Application:
     for coil insulation of high-voltage electrical machines
     for coil insulation of traction motors
     for case insulation of high-voltage electrical machines
     for case insulation of traction motors
Options:
     Produced thicknesses: from 0.08 mm to 0.20 mm
     Produced widths: from 15 mm to 870 mm
     Tapes are supplied in rolls and rollers with a diameter of (100 +10) mm, wound on a rigid sleeve with a diameter of at least 30 mm
     Breaks of tapes in rolls or rollers are not allowed
     Tape rollers are packed vertically in the manufacturer's carton
Advantages:
     Good electrical insulating properties
     Good mechanical characteristics when winding the section
     Improved strength characteristics
     Long shelf life in comparison with LSEP, LSK tapes
Appearance of rolls, rollers:
     The tape must be free of delaminations, foreign inclusions, without through holes
     The tape must be free of tears in the mica paper and backing
     Roller, roll must be smooth without blisters, bubbles
     The tape must be tightly wound on the sleeve, the sleeve must not be deformed
     The ends of the rollers or rolls must be cut evenly
     Tape in rolls, rollers should not have shifts along the edges
     The tape should unwind freely from a roll, roller without peeling the substrate
Box markings:
     Manufacturer's trademark
     Tape name
     Tape brand
     Tape thickness
     Tape width
     THAT
     Batch number
     Date of manufacture
     OTC seal
Storage conditions:
     The tape is stored in the manufacturer's boxes in closed, dry rooms.
     Storage of boxes on racks is provided (not less than 50 mm from the floor level and not less than 1 meter from existing heating and heating devices)
     Permissible temperature range from 5°C to 35°C
     Relative air humidity from 45% to 75%.

  Types of mica tapes and their technical characteristics

     1. LSK-110-TPl.
     Impregnation composition: epoxy-polyester composition.
     Hardening time: 2 hours.
     Tape thickness: 0.08 to 0.15 mm.
     Recommended temperature: 130°C.
     Characteristics:
         flexible
         easy to prepare forwork - unwind,
         melting allows to obtain a dense tape structure with excellent insulating properties.

     2. 1. LSK-110-Spl.
     The composition uses:
         epoxy compound.
         PET film,
         fiberglass.
    Tape thickness: 0.1 to 0.13 mm.
     Recommended temperature: 130°C.
     Applications:
         turn insulation of various motors and electric machines,
         body insulation.

     3. LSK.
     Binding composition: based on organosilicon substance.
     Tape thickness: 0.08 and 0.12 mm.
     Recommended temperature: up to 600°C.
     Scope of application: electrical insulation of cases and parts of electric machines and traction motors.

     4. LSK-SS.
     Binding composition: based on organosilicon substance.
     Product release form:
         rolls,
         rollers.
     Diameter: 100 mm.
     Width:15-870mm.
     Recommended temperature: up to 180°C.
     Scope of application: electrical insulation of electric motors and machines.

     5. LSK-110-TT.

     Hardening time: 2 hours.
     Recommended temperature: up to 160°C.
     Characteristics:
         very plastic material, when heated, it acquires a high level of flexibility.
     Heat resistance class: 155° C.

     6. LSKO-PM.

     Compound:
         polyamide film,
         fiberglass,
         mica paper,
         binder.
     Scope of application: Case electrical insulation of electrical equipment of various types.
     Product release form:
         rolls,
         rollers.
     Diameter: 100 mm.
     Width: 15-870 mm.
     Product thickness: from 0.11 to 0.17 mm.
     Recommended temperature: 180°C.

     7. LSU.

     Compound:
         polyester film,
         fiberglass,
         epoxy-polyester binder.
     Hardening time: 16 hours.
     Recommended temperature: 160° - 180° C.
     Scope of application: coil and body insulation.

     8. LIKO-TT.

     The composition uses: mica paper.
     Scope of application: turn insulation of equipment, traction motors.
     Tape thickness: 0.15 to 0.21 mm.
     Recommended temperature: 180°C.

     9. LSKN-135-Spl

     Ingredients: natural rubber.
     Scope of application: body winding of electrical appliances and machines.
     Tape thickness: 0.11 mm.
     Recommended temperature: 130, 155, 180°C. Depends on the type of impregnating composition.
     Characteristics: increased degree of thermal conductivity.

     10. LSKN-160-TT.

     Ingredients: Rubber.
     Tape thickness: 0.13 mm.
     Characteristics: increased degree of electrical insulation.